Kafrit PEX TA 1117 HD
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Kafrit NA Ltd. |
| Trademark: | Kafrit PEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GluOoU_Kafrit-PEX-TA-1117-HD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cross-linkable High Density Polyethylene Compound TA 1117 HD is for use in industrial applications. Crosslinked TA 1117 HD has a beneficial combination of high density and high gel content which result in excellent chemical, abrasion and heat resistance. The properties of TA 1117 HD make it a preferred choice for oil and gas, and other aggressive industrial applications. TA 1117 HD is suitable for continuous service exposed to hydrocarbons at operating temperatures of 200°F (93°C). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.947 | g/cm³ | ASTM D792 |
| Apparent Density | 0.54 | g/cm³ | ASTM D1895, ISO 60 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 1.0 | g/10 min | ASTM D1238 |
| Gel Content | 75 | % | ASTM D2765 |
| Moisture Content 1 | < 0.020 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Volatiles 2 | < 0.10 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 200 to 210 | °C | |
| Extruder Screw L/D Ratio | 25.0:1.0 | ||
| Extruder Screw Compression Ratio | 3.0:1.0 to 2.5:1.0 | ||
| Extruder Screw Temperature 3 | 70 to 90 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 22.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 250 | % | ASTM D638 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 154 to 177 | °C | |
| Cylinder Zone 2 Temp. | 165 to 188 | °C | |
| Cylinder Zone 3 Temp. | 177 to 200 | °C | |
| Cylinder Zone 4 Temp. | 188 to 200 | °C | |
| Die Temperature | 190 to 215 | °C |
| Note Message | |
|---|---|
| 1 . | Karl Fischer titration (SIL 4.4) |
| 2 . | SIL 4.3 |
| 3 . | Control of the screw temperature may improve processing results. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2866T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| NOVALAC RX®630 | Vyncolit N.V. | Phenolic | NOVALAC |
| GAPEX® RPP20EA HB | Ferro Corporation | PP, Unspecified | GAPEX® |
| Karina BLACK PVC COMPOUND -E 105900-48/ 1-B-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina BLACK PVC COMPOUND 750-48/1-GARAP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |