VAMPTER C 3528 V0
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPTER |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Glpih2_VAMPTER-C-3528-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UL 94 V0, blend PC/PBT 35% glass fiber reinforced, halogen free, good dimensional stability, good mechanical properties, very low toxicity and smoke |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 7000 | MPa | ASTM D790 |
| Flexural Strength | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 10 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 165 | °C | ASTM D648A |
| Vicat Softening Temperature | 150 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wanthane® WHT-2190 | Wanhua Chemical Group Co., Ltd. | TPU-Capro | Wanthane® |
| DOW™ LDPE PG 7004 (Injection Molding) | The Dow Chemical Company | LDPE | DOW™ LDPE |
| EMERGE™ PC 8230-31 | Trinseo | PC | EMERGE™ |
| HANWHA 3392 | Hanwha Chemical | HDPE | HANWHA |
| HOPELEN Y-120A | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |