PREPERM® L1000HF
| Category: | PPE , Polyphenylene Ether |
| Manufacturer: | Premix Oy |
| Trademark: | PREPERM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GlTdDY_PREPERM-L1000HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PREPERM® L1000HF is a special compound with elevated dielectric constants of 10. PREPERM® L1000HF is a special compound based on Premix proprietary PPE technology. Extremely low dissipation factor (< 0.001) makes PREPERM® L1000HF an excellent material for high frequency applications. PREPERM® L1000HF offers stable dielectric constant over wide frequency and wide temperature range. PREPERM® L1000HF is modified for injection moulding. Applications include structural parts for antennas in base stations, point to point, wlan, mobile phones etc. Devices made out of PREPERM® can operate at very high frequencies as PREPERM® offers stable performance even at 120 GHz. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.32 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (4.00 mm) | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 4.00 mm, Injection Molded) | 3.0 | % | ISO 527-2 |
| Flexural Modulus (4.00 mm) | 6200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 3.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 15 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 126 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 122 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1.00 GHz) | 10.0 | Internal method | |
| Dissipation Factor (1.00 GHz) | 8.0E-4 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 80.0 - 110 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Injection Pressure: High |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hylon® N2235HL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| Karina BLACK PVC COMPOUND -E 860D48/ 1-CY-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lucent PEI PEI-100 | Lucent Polymers, Inc. | PEI | Lucent PEI |
| Plenco 02369 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |
| Lucofin® 1492M | Lucobit AG | EBA | Lucofin® |