AKROMID® B3 2 RM-D black (3254) is a nonreinforced, UV-stabilised polyamide 6 with limited moisture absorption Applications are interior and exterior parts with improved impact strength in the automotive industry |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.10 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 30.0 | -- | cm³/10min | ISO 1133 |
| Spiral Flow | 65.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.80 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.7 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2500 | 1500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 60.0 | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | > 30 | > 100 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2300 | -- | MPa | ISO 178 |
| Flexural Stress | 70.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 11 | kJ/m² | |
| 23°C | 15 | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 100 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 2 | 225 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 3(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 10 K/min, DSC |
| 3 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TB120IR | Mando Advanced Materials Co., Ltd. | Nylon 6 | TEKAMID™ |
| TRIMID® N66-100NL | Polymer Technology and Services, LLC | Nylon 66 | TRIMID® |
| Nipol® NBR DN302 | Zeon Corporation | NBR | Nipol® NBR |
| AMTOPP TL40 | Inteplast Group | PP, Unspecified | AMTOPP |
| Sylvin 7868-85C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |