LNP™ THERMOCOMP™ MFB82I compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GlEHa2_LNP-THERMOCOMP-MFB82I-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF MFB82I is a compound based on Polypropylene resin containing Glass Fiber, Glass Bead. Also known as: LNP* THERMOCOMP* Compound MFX-100-10 MG-S Product reorder name: MFB82I |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.10 to 0.30 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 50.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 3800 | MPa | ISO 178 |
| Flexural Stress | 58.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 133 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.7E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.3E-4 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E665MZAA | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| SCANTEC PC S60R | Polykemi AB | PC | SCANTEC |
| Clariant Nylon 6 PA-211G33 | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| Cri-Line FDA-715 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| LUVOCOM® 20-0778 | Lehmann & Voss & Co. | PPA | LUVOCOM® |