Epocast 1619-A/B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gl0pSX_Epocast-1619-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DESCRIPTION: Epocast ® 1619-A/B epoxy syntactic is a low-density, self-extinguishing compound for potting fasteners in honeycomb structures. The lightweight epoxy can be poured or extruded through a 1/8 in. (3mm) nozzle orifice. Epocast ® 1619-A/B epoxy syntactic is resistant to water, fungus and most aircraft fluids and is qualified to BMS 5- 28, Type 19. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D1622 | ||
| -- 1 | 0.599 | g/cm³ | ASTM D1622 |
| -- | 0.698 | g/cm³ | ASTM D1622 |
| -- 2 | 0.998 | g/cm³ | ASTM D1622 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Modulus | 2410 | MPa | ASTM D695 |
| Compressive Strength (25°C) | 37.9 | MPa | ASTM D695 |
| Flammability | Nominal Value | ||
|---|---|---|---|
| Flammability | Self Extinguishing |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time (25°C) 3 | 20.0 - 50.0 | min | ASTM D2471 |
| Thermoset Mix Viscosity | ASTM D2196 | ||
| 25°C | Semi-Paste | ASTM D2196 | |
| 25°C 4 | Semi-Paste | ASTM D2196 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Extrudability (3.18 mm) | 350 | g/min | |
| Tensile Lap Shear - AL/AL | 8.62 | MPa | ASTM D1002 |
| Weight Gain 5 | ASTM D543 | ||
| Distilled Water : 25°C | 1.5 | % | ASTM D543 |
| Mil-M-5606 hydraulic fluid | 0.40 | % | ASTM D543 |
| Skydol 500-A : 25°C | 0.60 | % | ASTM D543 |
| TT-S-735, Type III test fluid : 25°C | 0.30 | % | ASTM D543 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 25 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity 6(25°C) | 400 | cP | ASTM D2196 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CURE SCHEDULE: Seven days at 77°F (25°C), or gel at room temperature plus five hours at 125°F (52°C). |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Hardener |
| 3 . | 50 gms |
| 4 . | Resin |
| 5 . | 24 hrs |
| 6 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC GX-1000 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| Formolene® 2510W | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Karina WHITE PVC COMPOUND -E 830-10/145-A-ERYB-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupolen 2421 H | LyondellBasell Industries | LDPE | Lupolen |
| Pier One POM AC GC25A BK | Pier One Polymers, Inc. | Acetal (POM) Copolymer | Pier One POM |