| Polyacetal copolymer with low viscosity in yellow color, easy processing, suitable for injection parts where it needs to be easily completed. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 24 to 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.8 to 2.0 | % | ASTM D955 |
| Ash Content | 1.4 | % | ASTM D2584 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 61.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 46 | % | ASTM D638 |
| Flexural Modulus | 2500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 160 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 100 | °C | |
| Melting Temperature | 170 | °C | ASTM D2117 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dissipation Factor | 6.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® TPP 512 | A. Schulman Inc. | TPO (POE) | POLYTROPE® |
| Sylvin 2911-55 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LARIPUR® LPR 9025 | COIM S.p.A. | TPU-Polyester | LARIPUR® |
| Karina GRAY PVC COMPOUND 702-DA-18/406-BZ-AS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petrothene® NA831000 | LyondellBasell Industries | LDPE | Petrothene® |