Sarlink® TPE EE-2270N-01
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GkXE04_Sarlink-TPE-EE-2270N-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE EE-2270N-01 is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is: extrusion. Sarlink®The main characteristics of TPE EE-2270N-01 are: sunlight resistance. Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shore A, 1 second, injection molding | 72 | ISO 868 | |
| Shore A, 5 seconds, injection molding | 68 | ISO 868 | |
| Shore A, 15 seconds, injection molding | 67 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Transverse flow : 100% strain | 2.11 | MPa | ISO 37 |
| Flow : 100% strain | 2.78 | MPa | ISO 37 |
| Tensile Stress 2 | ISO 37 | ||
| Transverse flow : Fracture | 10.6 | MPa | ISO 37 |
| Flow : Fracture | 7.70 | MPa | ISO 37 |
| Tensile Elongation 3 | ISO 37 | ||
| Transverse flow : Fracture | 770 | % | ISO 37 |
| Flow : Fracture | 610 | % | ISO 37 |
| Tear Strength 4 | ISO 34-1 | ||
| Transverse flow | 35 | kN/m | ISO 34-1 |
| Flow | 36 | kN/m | ISO 34-1 |
| Compression Set 5 | ISO 815 | ||
| 23°C, 22 hr | 24 | % | ISO 815 |
| 70°C, 22 hr | 52 | % | ISO 815 |
| 90°C, 70 hr | 65 | % | ISO 815 |
| 125°C, 70 hr | 81 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 6 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | 3.7 | % | ISO 188 |
| Flow : 110°C, 1008 hr | -0.40 | % | ISO 188 |
| Transverse flow : 100% strain 110°C, 1008 hr | 13 | % | ISO 188 |
| Flow : 100% strain 110°C, 1008 hr | 7.6 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | -0.90 | % | ISO 188 |
| Flow : 125°C, 168 hr | -3.9 | % | ISO 188 |
| Transverse flow : 100% strain 125°C, 168 hr | 11 | % | ISO 188 |
| Flow : 100% strain 125°C, 168 hr | 9.4 | % | ISO 188 |
| Change in Tensile Strain at Break in Air 7 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | -1.6 | % | ISO 188 |
| Flow : 110°C, 1008 hr | 0.0 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | -3.9 | % | ISO 188 |
| Flow : 125°C, 168 hr | -3.3 | % | ISO 188 |
| Change in Shore Hardness in Air | ISO 188 | ||
| Support a, 110°C, 1008 hr 8 | 4.9 | ISO 188 | |
| Support a, 110°C, 1008 hr 9 | 6.1 | ISO 188 | |
| Support a, 110°C, 1008 hr 10 | 6.4 | ISO 188 | |
| Support a, 125°C, 168 hr 11 | 3.3 | ISO 188 | |
| Support a, 125°C, 168 hr 12 | 4.0 | ISO 188 | |
| Support a, 125°C, 168 hr 13 | 4.4 | ISO 188 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 244 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 216 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Processing (Melt) Temp | 216 - 227 | °C | |
| Mold Temperature | 35.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 2 Temp. | 199 - 210 | °C | |
| Cylinder Zone 3 Temp. | 204 - 216 | °C | |
| Cylinder Zone 5 Temp. | 210 - 221 | °C | |
| Die Temperature | 216 - 227 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | Type 1, 510mm/min |
| 2 . | Type 1, 510mm/min |
| 3 . | Type 1, 510mm/min |
| 4 . | B method, right angle specimen (without cut), 510mm/min |
| 5 . | Type a |
| 6 . | Type 1 |
| 7 . | Type 1 |
| 8 . | 1 sec |
| 9 . | 5 sec |
| 10 . | 15 sec |
| 11 . | 1 sec |
| 12 . | 5 sec |
| 13 . | 15 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-403-M-G20 HF | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| MOSTEN MT 350 | UNIPETROL RPA | PP Homopolymer | MOSTEN |
| Flexalloy® 90-U656C-70 | Teknor Apex Company | PVC Elastomer | Flexalloy® |
| OTECH ALLOY XLO9141 - Riser Jacket | OTECH Corporation | TP, Unspecified | OTECH ALLOY |
| TechnoElast V D4000 I 2 sw | TechnoCompound GmbH | TPE | TechnoElast |