OKITEN® 222 A
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | DIOKI d.d. |
| Trademark: | OKITEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gig1k2_OKITEN-222-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OKITEN® 222 A is low density polyethylene, without slip agent, intended for extrusion of haevy duty blown film. OKITEN® 222 A is characterized by excellent processing properties and thermal stability. Extruded film has very good balance of stiffness, mechanical and optical properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | ISO 11501 | ||
| Across Flow : 140°C, 0.0500 mm | 22 | % | |
| Flow : 140°C, 0.0500 mm | 74 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 45 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 10.5 | MPa | |
| Break | 18.0 | MPa | |
| Tensile Strain (Break) | 750 | % | ISO 527-2 |
| Coefficient of Friction | ISO 8295 | ||
| vs. Itself - Dynamic | > 0.40 | ||
| vs. Itself - Static | > 0.40 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Thickness - Recommended / Available | 0.050 mm to 0.200 mm | ||
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 50 µm | 23.0 | MPa | |
| TD : Break, 50 µm | 21.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm | 280 | % | |
| TD : Break, 50 µm | 520 | % | |
| Trouser Tear Resistance | ISO 6383-1 | ||
| MD : 50 µm | 110 | N/mm | |
| TD : 50 µm | 74.0 | N/mm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm) | 36 | ASTM D2457 | |
| Haze (50.0 µm) | 5.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 175 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | dimensional change on heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIRASON™ 3530 | Mitsui Chemicals, Inc. | LDPE | MIRASON™ |
| Niplene C40 | Soredi S.p.a. | PP Homopolymer | Niplene |
| ALTECH® PA6 A 2015/512 GF15 IM UV | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| LNP™ STAT-LOY™ A30009 compound | SABIC Innovative Plastics | ABS | LNP™ STAT-LOY™ |
| Zytel® HTN 53C40HSL BK544 | DuPont Performance Polymers | HPPA | Zytel® HTN |