CAPRAN® 2500M is a 1.00 mil (25 micron) biaxially oriented nylon 6 film with a polymeric coating which provides enhanced adhesion to a variety of inks, coatings, and adhesives. Metallization adhesion is excellent when using "M" coated products.

General Information
Features	Good adhesion
Uses	Bi-axially Oriented Film
Forms	Films

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With Metal-Dynamic	0.23	ASTM D1894
With self-dynamics	0.75	ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	25	µm
secant modulus			ASTM D882
MD : 25 µm	2760	MPa	ASTM D882
TD : 25 µm	2760	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Break, 25 µm	255	MPa	ASTM D882
TD : Break, 25 µm	255	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Break, 25 µm	80	%	ASTM D882
TD : Break, 25 µm	80	%	ASTM D882
Oxygen Permeability (25°C)	0.71	cm³·mm/m²/atm/24 hr	ASTM D3985
Water Vapor Transmission Rate (25 µm, 38°C, 100% RH)	190	g·mm/m²/atm/24 hr	ASTM F1249

Optical	Nominal Value	Unit	Test Method
Gloss (20°, 25.4 µm)	90 - 140		ASTM D2457
Haze (25.4 µm)	2.3 - 3.4	%	ASTM D1003

Additional Information
Yield: 24000 in²/lbTensile Strength @ Break, ASTM D 882, MD & TD: 34000 to 42000 psiElongation @ Break, ASTM 882, MD & TD: 70 to 90%Secant Modulus, ASTM D 882, MD & TD: 350000 to 450000 psiGraves Tear (initial), ASTM D1004, MD & TD: 1100 to 1500 g/milDimensional Stability, ASTM D1204, 320°F, 5 mins, MD: 1.5 to 2.5% shrinkageDimensional Stability, ASTM D1204, 320°F, 5 mins, TD: 0.2 to 0.7% shrinkageCoefficient of Friction, ASTM D 1894: 0.60 to 0.90 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.18 to 0.27 vs Metal-DynamicOxygen Permeability, ASTM D 3985: 1.3 to 2.3 cc/100 in²/dayWater Vapor Transmission, ASTM F 1249: 11 to 13 g/100 in²/daySurface Tension, ASTM 2578, minimum, treated side: >/= 56 dynes/cmSurface Tension, ASTM 2578, Minimum, untreated side: >/= 50 dynes/cm

Additional Information

Yield: 24000 in²/lbTensile Strength @ Break, ASTM D 882, MD & TD: 34000 to 42000 psiElongation @ Break, ASTM 882, MD & TD: 70 to 90%Secant Modulus, ASTM D 882, MD & TD: 350000 to 450000 psiGraves Tear (initial), ASTM D1004, MD & TD: 1100 to 1500 g/milDimensional Stability, ASTM D1204, 320°F, 5 mins, MD: 1.5 to 2.5% shrinkageDimensional Stability, ASTM D1204, 320°F, 5 mins, TD: 0.2 to 0.7% shrinkageCoefficient of Friction, ASTM D 1894: 0.60 to 0.90 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.18 to 0.27 vs Metal-DynamicOxygen Permeability, ASTM D 3985: 1.3 to 2.3 cc/100 in²/dayWater Vapor Transmission, ASTM F 1249: 11 to 13 g/100 in²/daySurface Tension, ASTM 2578, minimum, treated side: >/= 56 dynes/cmSurface Tension, ASTM 2578, Minimum, untreated side: >/= 50 dynes/cm

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Honeywell
Trademark:	Capran®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	GhZGP7_Capran-2500M.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 1305	RTP Company	PPS	RTP
Medalist® MD-305	Teknor Apex Company	TPE	Medalist®
Bayblend® M303 FR	Covestro - Polycarbonates	PC+ABS	Bayblend®
EPAMOULD 295A83W40	Epaflex Polyurethanes S.R.L.	TPU-Polyester	EPAMOULD
CYCOLAC™ FXS610SK resin	SABIC Innovative Plastics Europe	ABS	CYCOLAC™