Synthos EPS® 2040FR/CZ
| Category: | PS (EPS) , Expanded Polystyrene |
| Manufacturer: | Synthos S.A. |
| Trademark: | Synthos EPS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GhCgD8_Synthos-EPS-2040FR-CZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Synthos EPS®/CZ types 0513FR, 0514FR 0822FR, 1640FR and 2040FR are self-extinguishing expandable polystyrene EPS with low content of pentane. The materials are formed by spherical polystyrene particles that contain a flame retardant system (content of HBCD < 0,5%) and a hydrocarbon blowing agent. Their surface is treated against gluing during processing and the formation of electrostatic charge. Due to the content of halogenated flame retardant and the residual blowing agent, the product is unsuitable for objects intended for direct contact with food. Synthos EPS® 1640FR/CZ (Koplen 1640FR) oraz Synthos EPS® 2040FR/CZ (Koplen 2040FR) is mainly used for production of high volume blocks with low-density; of cutted boards and profiles from the blocks for a thermal insulation e.g. building objects. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Density 1 | 0.02 to 0.04 | g/cm³ | Internal Method |
| Moisture Content | < 10000 | ppm | Internal Method |
| Particle Size - >95% between | 2.00 to 4.00 | mm | Internal Method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Reaction to Fire | |||
| -- | B1 | DIN 4102 | |
| -- | Class E | EN 13501-1 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blowing Agent | < 5.5 | wt% | Internal Method |
| Note Message | |
|---|---|
| 1 . | The typical bulk density indicates values obtained during single-step pre-foaming on continuous pre-foaming devicesLower values of bulk density can be achieved only after multiple pre-expansion. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Andur M-95 AS/Curative | Anderson Development Company | PUR-MDI | Andur |
| Karina WHITE PVC COMPOUND 803-10/34-A-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SD POLYCA™ 875G20F | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |
| Badatron® PPS GF30 TF/SIM15 | Bada AG | PPS | Badatron® |
| Moplen HP544T | LyondellBasell Industries | PP Homopolymer | Moplen |