INNOMID ® CS 6-9000 HI is an unfilled, elastomer modified polyamide (PA-6) compound. This grade is available in nature and custom coloured form. Recommended application INNOMID ® CS 6-9000 HI is recommended for producing injection moulded products, where the required properties are high stiffness and good impact resistance. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.13 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 113 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/2 |
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 1800 | MPa | ISO 178 |
| Flexural Stress 2 | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 525 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 220 - 260 | °C | |
| Middle Temperature | 220 - 260 | °C | |
| Front Temperature | 220 - 260 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding Pressure: 50-100% of actual injection pressure |
| Note Message | |
|---|---|
| 1 . | Type 1A, 2.0 mm/min |
| 2 . | Type 1A, 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2990-60 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Hostacom M2 V17 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Karina BLACK PVC COMPOUND 75930-48/ 1-F-AC-LF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lotrène® LLDPE Q1018H | QATOFIN Company Limited | LLDPE | Lotrène® LLDPE |
| Sylvin 9915-60 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |