Arlon® 1000
| Category: | PTFE+PI , Polytetrafluoroethylene + PI |
| Manufacturer: | Greene, Tweed & Co. |
| Trademark: | Arlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GgrE6a_Arlon-1000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Greene, Tweed's Arlon® 1000, a tough, hig temperature, semi-crystalline thermoplastic, offers a unique combination of mechanical, thermal and chemical propertier. Arlon 1000 features superior compressive strength and minimum creep, as well as broad chemical resistance. Arlon is an excellent choice for applications such as valve seats and bushings greater abrasion resistance and lower wear and better fatigue properties than other thermoplastics. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 104 | ASTM D785 | |
| Durometer Hardness (Shore D) | 88 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 0.5% Secant | 4240 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 108 | MPa | |
| Break | 96.5 | MPa | |
| Tensile Elongation (Break) | 35 | % | ASTM D638 |
| Flexural Modulus - 0.5% Secant | 4140 | MPa | ASTM D790 |
| Flexural Strength | 174 | MPa | ASTM D790 |
| Compressive Strength 1 | 131 | MPa | ASTM D695 |
| Shear Strength | ASTM D732 | ||
| -- 2 | 85.5 | MPa | |
| -- 3 | 85.5 | MPa | |
| Coefficient of Friction 4(vs. Itself - Dynamic) | 0.29 | ASTM G77 | |
| Deformation Under Load | 0.0900 | % | ASTM D621 |
| Wear Factor | 100 | 10^-8 mm³/N·m | ASTM G77 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 177 | °C | ASTM D648 |
| CLTE - Flow | ASTM E228 | ||
| < 149°C | 4.7E-5 | cm/cm/°C | |
| > 149°C | 1.4E-4 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Break |
| 2 . | Transverse |
| 3 . | Axial |
| 4 . | PV + 12600 psi-ft/in |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermoset Plastics 265 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| Utomer UT81P85A | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyether | Utomer |
| AKROMID® A3 GF 40 1 natural (2381) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Lupolen 2421 H | LyondellBasell Industries | LDPE | Lupolen |
| Sylvin 9600-80 Clear 896 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |