DURACON® SW-01LV
| Category: | Acetal (POM) Copolymer+PE , Acetal (POM) Copolymer + PE |
| Manufacturer: | Polyplastics Co., Ltd. |
| Trademark: | DURACON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ggi3Mz_DURACON-SW-01LV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low VOC, High Sliding |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 6.00 | cm³/10min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress | 50.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 20 | % | ISO 527-2 |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| Flexural Stress | 75.0 | MPa | ISO 178 |
| Coefficient of Friction 1(Dynamic) | 0.22 | JIS K7218 | |
| Wear Factor | JIS K7218 | ||
| 0.060 MPa, 0.15 m/sec 2 | 400 | 10^-8 mm³/N·m | JIS K7218 |
| 0.060 MPa, 0.15 m/sec 3 | 500 | 10^-8 mm³/N·m | JIS K7218 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.4 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Linear thermal expansion coefficient | Internal method | ||
| Flow : 23 to 55°C | 1.1E-4 | cm/cm/°C | Internal method |
| Lateral : 23 to 55°C | 1.1E-4 | cm/cm/°C | Internal method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Color Number | CF2001 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Pressure | 49.0 - 98.0 | MPa | |
| Screw Speed | 100 - 150 | rpm |
| Injection instructions |
|---|
| Injection speed: 5-50 mm/sInjection Holding pressure: Gate sealing time + alphaCooling: Plasticizing time or ejection capable time |
| Note Message | |
|---|---|
| 1 . | vs. M90-44, 0.06 MPa, 15 cm/s |
| 2 . | vs M90-44, Material Side |
| 3 . | vs M90-44, M90-44 Side |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Synprene™ RT-5155 RoHS Natural | PolyOne Corporation | SBC | Synprene™ |
| TOTAL Polypropylene PPH 3480Z | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| APEX® 157-V | Teknor Apex Company | PVC, Flexible | APEX® |
| CP PRYME® Nylon 6 N100LZ NAT | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |
| Generic Nylon 66+Nylon 6I/6T - Glass Fiber | Generic | Nylon 66+Nylon 6I/6T | Generic |