INNOPOL® PP CS 1-3140 MA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GgCFnd_INNOPOL-PP-CS-1-3140-MA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL ® CS 1-3140 MA is a 40 % talc-filled polypropylene homopolymer compound. This grade is available in nature and custom coloured form. Recommended application INNOPOL ® CS 1-3140 MA is recommended especially for producing products, where high stiffness, long term heat stability and excellent processability are required. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 31.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.5 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 4000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 1.5 | kJ/m² | ISO 179/1eA |
| 23°C | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 9.0 | kJ/m² | ISO 179/1eU |
| 23°C | 20 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 133 | °C | ISO 75-2/B |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ISO 306/A120 |
| -- | 90.0 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 250 | °C | |
| Middle Temperature | 190 - 250 | °C | |
| Front Temperature | 190 - 250 | °C | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold Pressure: 30 to 100% of injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 MV 14 FR 4 K1681 | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| SEPAZ™ K115HF | Mando Advanced Materials Co., Ltd. | PPS | SEPAZ™ |
| Vital-Line SHM4200 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| NYLEM® 66 GFR 30 | EMAS Plastik San.Tic.AS. | Nylon 66 | NYLEM® |
| KEBAFLEX® S 95 A.01 | BARLOG plastics GmbH | TES | KEBAFLEX® |