Electrafil® PA6/6 03002 A MB
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gg52Ng_Electrafil-PA6-6-03002-A-MB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Electrafil®PA6/6 03002 A MB is a polyamide 66 (nylon 66) product, which contains glass fiber reinforced materials and fillers. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.90 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 111 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 84.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus | 3620 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 110 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 150 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 252 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 220 | °C | ASTM D648 |
| CLTE - Flow | 7.9E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 - 1.0E+3 | ohms | ASTM D257 |
| Volume Resistivity | 10 - 1.0E+3 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 277 - 288 | °C | |
| Front Temperature | 271 - 282 | °C | |
| Nozzle Temperature | 271 - 282 | °C | |
| Processing (Melt) Temp | 277 - 288 | °C | |
| Mold Temperature | 79.4 - 104 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well vented moldMoisture Content, as received: Product is packaged at 0.2% or less. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polymist® XPP 515-S | Solvay Specialty Polymers | PTFE | Polymist® |
| Chemical Resources BPP100 | Chemical Resources, Inc. | PP Impact Copolymer | Chemical Resources |
| Colorite SF 6011SF | Colorite Polymers | PVC, Unspecified | Colorite SF |
| FERREX® GPP30CS81HB NATURAL | Ferro Corporation | PP Copolymer | FERREX® |
| Karina PVC COMPOUND TR-450D42/347-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |