RALUPOL® UP 4566
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | RASCHIG GmbH |
| Trademark: | RALUPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gf8cUR_RALUPOL-UP-4566.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glass-fibre reinforced Polyester moulding compound Low mould shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability Primary application(s): Lamp holders for automobile halogen bulbs This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.00 to 2.20 | g/cm³ | ISO 1183 |
| Apparent Density | 0.90 to 1.10 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow 1 | 0.30 to 0.60 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 0.60 | % | ISO 62 |
| Post Shrinkage 2 | < 0.10 | % | ISO 2577 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Service Temperature | IEC 60216 | ||
| <50 h | 200 | °C | |
| 20,000 h | 160 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 10.0 | MPa | |
| Compression Molding Temperature | 165 to 180 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (Compression Molded) | 16000 to 20000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 60.0 to 80.0 | MPa | ISO 178 |
| Compressive Stress | 150 to 200 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Compression Molded) | 2.0 to 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (Compression Molded) | 3.0 to 4.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | > 200 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 150 to 170 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 100°C) | 1.0E-5 to 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.90 to 1.1 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 to 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 to 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 25 to 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 6.00 5.00 | ||
| 1 MHz | 5.00 4.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.010 to 0.030 | ||
| 1 MHz | 0.010 to 0.030 | ||
| Arc Resistance | PLC 4 | ASTM D495 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by RASCHIG) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Middle Temperature | 50.0 to 70.0 | °C | |
| Front Temperature | 80.0 to 100 | °C | |
| Processing (Melt) Temp | 100 to 115 | °C | |
| Mold Temperature | 165 to 180 | °C | |
| Back Pressure | 1.00 to 1.50 | MPa | |
| Screw Speed | 70 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-1402G | Teknor Apex Company | TPE | Telcar® |
| Toraycon® 5101G-30U | Toray Resin Company | PBT | Toraycon® |
| Geon™ Vinyl Rigid Molding M3900 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| Karina BLACK PVC COMPOUND 830-48/1-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MAXAMID™ EPDM6G33-NC010 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |