Lucky Enpla LAY1000 9309
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Lucky Enpla Co LTD |
| Trademark: | Lucky Enpla |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GefP9d_Lucky-Enpla-LAY1000-9309.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lucky Enpla LAY1000 9309 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. Typical application areas are: electrical/electronic applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 - 0.65 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 50.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2160 | MPa | ASTM D790 |
| Flexural Strength 3 | 73.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (3.18 mm) | 470 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 115 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 250 - 270 | °C | |
| Middle Temperature | 260 - 280 | °C | |
| Front Temperature | 265 - 285 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Back Pressure | 0.490 - 2.94 | MPa | |
| Screw Speed | 30 - 50 | rpm |
| Injection instructions |
|---|
| Resin Temperature: 250-270°CInjection Pressure (1st Pressure): 700-1200 kg/cm²Injection Pressure (2nd Pressure): 500-900 kg/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 10 mm/min |
| 3 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT REGRIND PA66 101L-300RG | NEXT Specialty Resins, Inc. | Nylon 66 | NEXT REGRIND |
| Formolon® 10 | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |
| ICORENE® CX-350S | ICO Polymers NA, A Division of A. Schulman | XLPE | ICORENE® |
| PLUSTEK RB703 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| Mitsui EPT™ 2060M | Mitsui Chemicals, Inc. | EPDM | Mitsui EPT™ |