Durethan® BKV 25 FN01 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GeKFhu_Durethan-BKV-25-FN01-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 25 % glass fibers, injection molding, halogen free flame retardant, improved flowability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.39 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 260°C, 2.00 mm 1 | 0.60 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.10 | -- | % | |
| Flow : 260°C, 2.00 mm 3 | 0.30 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.10 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9500 | 5600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 130 | 80.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.8 | 6.8 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 9200 | 5800 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | -- | 130 | MPa | |
| 23°C 6 | 210 | 140 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 3.3 | 5.4 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA6, GFHR, 10-090, GF25; ISO1043-PA GF FR (30+40+72) | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.070 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 60 | 65 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | < 10 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 55 | 60 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 202 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 213 | -- | °C | ISO 306/B120 |
| Ball Pressure Test (210°C) | Pass | -- | IEC 60695-10-2 | |
| Melting Temperature 8 | 222 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 4.0E+15 | -- | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 5.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 39 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (CTI) | PLC 0 | -- | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | V-0 | -- | ||
| 1.50 mm | V-0 5VA | -- | ||
| 3.00 mm | V-0 5VA | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.750 mm | 960 | -- | °C | |
| 1.50 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 775 | -- | °C | |
| 3.00 mm | 775 | -- | °C |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 34S5301 | The Matrixx Group, Inc. | PBT | Matrixx |
| tivilon® F 65 Dx 4 | API SpA | TPV | tivilon® |
| BONDYRAM® 6000 | Polyram Ram-On Industries | ABS | BONDYRAM® |
| KOPLA PA6 KYE1210 | KOPLA Co., Ltd. | Nylon 6+PP | KOPLA PA6 |
| Jam PE 524H1 | Jam Petrochemical Company | HDPE, HMW | Jam PE |