Xuchuan A-9088A/B-6088
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Xuchuan Chemical (Suzhou) Co., Ltd |
| Trademark: | Xuchuan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GdAgE5_Xuchuan-A-9088A-B-6088.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Xuchuan A-9088A/B-6088 is a Thermoplastic Polyurethane Elastomer (Polyester) (TPU-Polyester) product. It is available in Asia Pacific. Typical application: Consumer Goods. Primary characteristic: high hardness. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density | 0.380 to 0.480 | g/cm³ | |
| Density | |||
| A-9088A : 40°C | 1.010 to 1.020 | g/cm³ | |
| B-6088 : 40°C | 1.080 to 1.200 | g/cm³ | |
| Viscosity | |||
| A-9088A : 40°C | 1.00 to 1.40 | Pa·s | |
| B-6088 : 40°C | 0.600 to 0.800 | Pa·s |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Williams Abrasion | 300 to 400 | cc/php |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Cream Time | 6.0 to 8.0 | sec | |
| End of Rise Time | 50.0 to 60.0 | sec |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Free Rise Foam Density | 170 to 200 | kg/m³ | |
| Preheat Temperature | |||
| Part A | 50 to 60 | °C | |
| Part B | 50 to 60 | °C | |
| Preheat Time | |||
| Part A | 6.0 to 8.0 | hr | |
| Part B | 6.0 to 8.0 | hr | |
| Processing Temperature | |||
| Part A | 40 to 45 | °C | |
| Part B | 38 to 42 | °C |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 83 to 93 |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength (Break) | 10.0 to 15.0 | MPa | |
| Tensile Elongation (Break) | 150 to 260 | % | |
| Tear Strength | 35.0 to 40.0 | kN/m |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 110 | ||
| Demold Time | 5.0 to 7.0 | min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 45.0 to 55.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 910 | Salflex Polymers Ltd. | HDPE | Salflex |
| Shin-Etsu Elastomer KE-571U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| TULAMID® PA-SV20 | UCC Shchekinoazot | Nylon 6 | TULAMID® |
| ALTECH® PA66 A 2015/710 GF15 IM | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Fainplast PVC PH 65/A | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |