Braskem PE TX7003
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GccUq0_Braskem-PE-TX7003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TX7003 is a low-density, high molecular-weight polyethylene that offers high mechanical strength. The product's characteristics allow for a high versatility and use in various applications due to its easy processing and high compatibility with other types of polyethylene. TX7003 resin shows excellent performance with conventional extruders and low energy consumption during processing, which allows producing packaging with dimensional uniformity and excellent surface finishing. This product is identified as PE 115 according to ASTM D-4976-04a standard specification. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.922 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.27 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 50 µm, Blown Film | 140 | MPa | |
| 2% Secant, TD : 50 µm, Blown Film | 150 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 50 µm, Blown Film | 30.0 | MPa | |
| TD : Break, 50 µm, Blown Film | 25.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm, Blown Film | 370 | % | |
| TD : Break, 50 µm, Blown Film | 680 | % | |
| Dart Drop Impact (50 µm, Blown Film) | 190 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, Blown Film | 300 | g | |
| TD : 50 µm, Blown Film | 220 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45°, 50.0 µm, Blown Film | 47 | ||
| 60°, 50.0 µm, Blown Film | 69 | ||
| Haze (50.0 µm, Blown Film) | 12 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 205 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Supol HE151E | LyondellBasell Industries | Polyolefin, Unspecified | Supol |
| THERMOLAST® K TF8BNA (Series: FC/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Algoflon® L206 | Solvay Specialty Polymers | PTFE | Algoflon® |
| Grivory® HTV-6H1 black 9205 | EMS-GRIVORY | Nylon 6I/6T | Grivory® |
| Sylvin 8999-73 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |