LNP™ LUBRICOMP™ RL002 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GbzskL_LNP-LUBRICOMP-RL002-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* RL002 is a compound based on Nylon 66 resin containing 10% PTFE. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RL-4020 Product reorder name: RL002 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 2.2 | % | |
| Across Flow : 24 hr | 2.6 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.94 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3090 | MPa | ASTM D638 |
| -- | 3180 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 75.1 | MPa | ASTM D638 |
| Yield | 73.0 | MPa | ISO 527-2 |
| Break | 74.7 | MPa | ASTM D638 |
| Break | 73.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 14 | % | ASTM D638 |
| Yield | 17 | % | ISO 527-2 |
| Break | 14 | % | ASTM D638 |
| Break | 18 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3040 | MPa | ASTM D790 |
| -- | 2840 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 112 | MPa | ASTM D790 |
| -- | 89.4 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.27 | ||
| vs. Itself - Static | 0.23 | ||
| Wear Factor - Washer | 49.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 32 | J/m | ASTM D256 |
| 23°C 2 | 4.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 900 | J/m | ASTM D4812 |
| 23°C 3 | 59 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 3.59 | J | ASTM D3763 |
| -- | 4.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 76.1 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 74.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.3E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCW-8880N-12 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Yuyao PPO GFN2-101 | Yuyao Tenglong Plastics Co., Ltd. | PPE+PS | Yuyao PPO |
| Geon™ Vinyl Wire & Cable WY594B | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| ISOTHANE® 1085AF | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |
| LNP™ THERMOTUF™ WF006N compound | SABIC Innovative Plastics Asia Pacific | PBT | LNP™ THERMOTUF™ |