LNP™ THERMOCOMP™ LF005 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GbGn11_LNP-THERMOCOMP-LF005-compound-87835.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP LF005 is a compound based on Polyetheretherketone resin containing 25% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound LF-1005 Product reorder name: LF005 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.50 to 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 1.0 to 1.2 | % | ASTM D955 |
| Across Flow : 24 hr | 1.1 | % | ISO 294-4 |
| Flow : 24 hr | 0.64 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11700 | MPa | ASTM D638 |
| -- | 11400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 157 | MPa | ASTM D638 |
| Yield | 158 | MPa | ISO 527-2 |
| Break | 157 | MPa | ASTM D638 |
| Break | 158 | MPa | ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 2.7 | % | |
| Break | 2.7 | % | |
| Flexural Modulus | |||
| -- | 8960 | MPa | ASTM D790 |
| -- | 8600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 248 | MPa | ASTM D790 |
| -- | 243 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 91 | J/m | ASTM D256 |
| 23°C 2 | 8.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 930 | J/m | ASTM D4812 |
| 23°C 3 | 60 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 14.6 | J | ASTM D3763 |
| -- | 3.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 239 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 5.4E-6 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 5.2E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 1.8E-6 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 1.9E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propilven J-844 | Propilven, S.A. | PP Impact Copolymer | Propilven |
| SABIC® LDPE Powder 1965P3 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| ALCOM® PP 620/8 GF30 PTFE15 | ALBIS PLASTIC GmbH | PP Homopolymer | ALCOM® PP |
| AKROTEK® PK-VM GF 60 natural (4923) | AKRO-PLASTIC GmbH | PK-Aliphatic | AKROTEK® |
| APEX® 3703-78NT1 | Teknor Apex Company | PVC, Flexible | APEX® |