Multi-Flex® TPE A6202 MR
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Multibase, A Dow Corning Company |
| Trademark: | Multi-Flex® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GayFun_Multi-Flex-TPE-A6202-MR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Multi-Flex® TPE A6202 MR is a Thermoplastic Elastomer (TPE) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Automotive. Primary characteristic: scratch resistant. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 15 sec) | 65 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 6.00 | MPa | ISO 37 |
| Tensile Elongation (Break) | 680 | % | ISO 37 |
| Tear Strength | 35 | kN/m | ISO 34-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 188 | °C | |
| Middle Temperature | 193 | °C | |
| Front Temperature | 202 | °C | |
| Nozzle Temperature | 210 | °C | |
| Processing (Melt) Temp | 210 | °C | |
| Mold Temperature | 26.7 to 43.3 | °C | |
| Injection Rate | Moderate-Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Novalloy-E E70 | Daicel Polymer Ltd. | ABS | Novalloy-E |
| Badamid® PA612 GF33 | Bada AG | Nylon 612 | Badamid® |
| Calprene® 718 | Dynasol Elastomers | SBS | Calprene® |
| EBAC+® SP1903 | Westlake Chemical Corporation | EBA | EBAC+® |
| Karina BLACK PVC COMPOUND 901D48/ 7-C-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |