POLIMAXX 2563PCXTA6
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | IRPC Public Company Limited |
| Trademark: | POLIMAXX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GZztcC_POLIMAXX-2563PCXTA6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 2563PCXTA6 is a PP Block co-polymer with 30% Talcum filler for injection molding process, features high melt flow, high flexural modulus and high heat resistance with UV Stabilizer. It is suitable for auto parts and electrical appliances. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 88 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 22.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 8.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 3240 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 38.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) (23°C) | 4.90 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 140 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Processing (Melt) Temp | 190 to 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC8MLZ (Series: AD1) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Latigea B01 F1 | LATI S.p.A. | PLA | Latigea |
| Indothene 1005FY20 | Reliance Industries Limited | LDPE | Indothene |
| Jampilen HP501M | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| Neoflex™ 7070 | Zylog Plastalloys Pvt. Ltd. | TPE | Neoflex™ |