SABIC® PPcompound G3230A
| Category: | PP, Unspecified , Polypropylene Homopolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GZfrqx_SABICPPcompoundG3230A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® PPCOMPOUND G3230A is a general purpose, 30% glass filled, chemically coupled, heat stabilized homopolymer polypropylene compound. The IMDS ID is 109612410 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction : 23°C, 48 hours | 0.70 | % | Internal method |
| Flow direction : 23°C, 48 hours | 0.40 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6590 | MPa | ASTM D638 |
| -- | 6500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 83.0 | MPa | ASTM D638 |
| Fracture | 85.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Fracture 3 | 2.7 | % | ASTM D638 |
| Fracture | 3.3 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 4 | 5130 | MPa | ASTM D790 |
| 64.0mm span 5 | 6600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 6 | 11 | kJ/m² | ISO 179/1eA |
| 23°C 7 | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.20 mm 8 | 81 | J/m | ASTM D256 |
| -30°C 9 | 11 | kJ/m² | ISO 180/1A |
| 23°C 10 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact 11(23°C, 3.20 mm) | 570 | J/m | ASTM D4812 |
| Instrumented Dart Impact 12(23°C, Energy at Peak Load) | 7.65 | J | ASTM D3763 |
| Dart Drop Impact 13(23°C) | 0.520 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 159 | °C | ASTM D648 |
| 0.45 MPa, not annealed 14 | 160 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 3.20mm | 150 | °C | ASTM D648 |
| 1.8 MPa, not annealed 15 | 150 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 164 | °C | ISO 306/A50 |
| Coefficient of Linear Thermal Expansion | ISO 11359-2 | ||
| Flow : -30 to 100°C | 5.60 | µm/Mk | ISO 11359-2 |
| Transverse : -30 to 100°C | 160 | µm/Mk | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 190 - 230 | °C | |
| Middle Temperature | 200 - 250 | °C | |
| Front Temperature | 210 - 270 | °C | |
| Nozzle Temperature | 210 - 270 | °C | |
| Processing (Melt) Temp | 210 - 270 | °C | |
| Mold Temperature | 15.0 - 60.0 | °C | |
| Back Pressure | 1.00 - 1.50 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 80*10*4mm, Cut |
| 7 . | 80*10*4 mm, Cut |
| 8 . | 63.5*12.7*3.2mm, Cut |
| 9 . | 80*10*4mm, Cut |
| 10 . | 80*10*4mm, Cut |
| 11 . | 63.5*12.7*3.2mm, Cut |
| 12 . | 2.20 m/sec |
| 13 . | 0.625"d tup |
| 14 . | 80*10*4mm, Cut |
| 15 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 TC-I-15 | RTP Company | PC | RTP |
| Sumikon® EME-9300HX | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| Borealis PP RP970 | Borealis AG | PP, Unspecified | Borealis PP |
| ELASTOSIL® R plus 4001/40 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| Sylvin 8739-65FU Brown 7348 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |