HOPELEN SFO-130BA-1
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | HOPELEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GZ8bZH_HOPELEN-SFO-130BA-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HOPELEN SFO-130BA-1 is homo polymer resin produced by the polymerization of propylene. This grade is designed to be processed in BOPP film applications. This grade shows good transparence, anti-static and printing properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 35.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 100 | % | ASTM D638 |
| Flexural Modulus | 1520 | MPa | ASTM D790 |
| Coefficient of Friction (Blown Film) | < 1.0 | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 150 | °C | ASTM D1525 |
| Melting Temperature | 165 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (30.0 µm, Blown Film) | < 0.90 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TB120G30 | Mando Advanced Materials Co., Ltd. | Nylon 6 | TEKAMID™ |
| Elastollan® S 90 A | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| EnCom ABS 5035 | EnCom, Inc. | ABS | EnCom |
| Pujie CPE-8090 | Zhanhua Pujie Chemical Technology Co.,Ltd | CPE | Pujie |
| LG ASA LI923P | LG Chem Ltd. | ASA | LG ASA |