3M™ Dyneon™ Fluoroelastomer FC 1640

Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	3M Advanced Materials Division
Trademark:	3M™ Dyneon™ Fluoroelastomer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	GYr8Q5_3MDyneonFluoroelastomerFC1640.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
3M™ Dyneon™ Fluoroelastomer FC 1640 is a dipolymer made from hexafluoropropylene and vinylidene fluoride. It is a raw gum without curatives. Special Features Composition: dipolymer of vinylidene fluoride and hexafluoropropylene Process targets: transfer and compression moulding, extrusion, calendering and coatings Medium viscosity gum stock without incorporated curatives Amine and bisphenol curable Typical Applications 3M™ Dyneon™ Fluoroelastomer FC 1640 is suitable for all sorts of finished products: O-rings, moulded parts, including metal bonding products, extrudates and calendered sheets, depending on the curative package and compound recipe used.

Message

3M™ Dyneon™ Fluoroelastomer FC 1640 is a dipolymer made from hexafluoropropylene and vinylidene fluoride. It is a raw gum without curatives.

Special Features

Composition: dipolymer of vinylidene fluoride and hexafluoropropylene

Process targets: transfer and compression moulding, extrusion, calendering and coatings

Medium viscosity gum stock without incorporated curatives

Amine and bisphenol curable

Typical Applications
3M™ Dyneon™ Fluoroelastomer FC 1640 is suitable for all sorts of finished products: O-rings, moulded parts, including metal bonding products, extrudates and calendered sheets, depending on the curative package and compound recipe used.

General Information
Features	Medium viscosity
Uses	O-rings Metal bonding Sheet Coating application
Forms	Particle
Processing Method	Extrusion Resin transfer molding Coating Compression molding Calendering

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.80	g/cm³	Internal method
Mooney Viscosity (ML 1+10, 121°C)	35	MU	Internal method
Fluorine Content	66	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	73		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹(100% Strain)	6.70	MPa	ASTM D412A
Tensile Strength ²	13.7	MPa	ASTM D412A
Tensile Elongation ³(Break)	170	%	ASTM D412A
Compression Set (200°C, 70 hr)	15	%	ASTM D1414

Note Message
1 .	D mould
2 .	Die D
3 .	D mould

Resin Grade	Manufacturer	Category	Trademark
TRIBS® 640U	Samyang Corporation	ABS	TRIBS®
DOW™ Electrical & Telecommunications DGDL-3479 BK	The Dow Chemical Company	HDPE	DOW™ Electrical & Telecommunications
Hoffman PVC 117-110	Hoffman Plastic Compounds Inc.	PVC, Rigid	Hoffman PVC
Huafon JF-HSY-ADP2	Huafon Group Co., Ltd.	PUR, Unspecified	Huafon
INEOS LDPE 20N430	INEOS Olefins & Polymers Europe	LDPE	INEOS LDPE