LNP™ THERMOCOMP™ LX09404 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GYqm2G_LNP-THERMOCOMP-LX09404-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP LX09404 is a compound based on Polyetheretherketone resin containing Carbon Fiber. Also known as: LNP* THERMOCOMP* Compound LX09404 Product reorder name: LX09404 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr, 50% RH) | 0.41 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 41500 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 280 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.3 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 29700 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 424 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 93 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 830 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 332 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA66-8018-BK | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| RTP 2283 HF TFE 10 | RTP Company | PEEK | RTP |
| SILVER® SA-3130 | Guangdong Silver Age Sci & Tech. Co., Ltd | TPE | SILVER® |
| Vi-Chem PVC VSR87E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Karina BROWN PVC COMPOUND 800-36/61-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |