Tufpet PBT FEX70
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Tufpet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GYgh41_Tufpet-PBT-FEX70.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tufpet PBT FEX70 is a Polybutylene Terephthalate (PBT) material filled with 70% steel. It is available in North America for injection molding. Important attributes of Tufpet PBT FEX70 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 3.29 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0 to 1.2 | % | ASTM D955 |
| Water Absorption (Saturation, 23°C) | 0.38 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 43.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus | 7350 | MPa | ASTM D790 |
| Flexural Strength | 76.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 39 | J/m | ASTM D256 |
| Unnotched Izod Impact | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 194 | °C | |
| 1.8 MPa, Unannealed | 130 | °C | |
| RTI Elec (1.67 mm) | 75.0 | °C | UL 746 |
| RTI Imp (1.67 mm) | 75.0 | °C | UL 746 |
| RTI Str (1.67 mm) | 75.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.2E+2 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.67 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 230 to 303 | °C | |
| Middle Temperature | 230 to 303 | °C | |
| Front Temperature | 230 to 303 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Injection Pressure | 81.4 | MPa | |
| Screw Speed | 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 2206-15 CR-SX | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| WELLAMID Nylon 6600 MR 409 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Geon™ 210 Series 217 Blending Resin | Mexichem Specialty Resins, Inc. | PVC Homopolymer | Geon™ 210 Series |
| LAMIGAMID® 200 | Schwartz Technical Plastic | Nylon 66 | LAMIGAMID® |
| Braskem PE CP 393 | Braskem | PP Impact Copolymer | Braskem PE |