POLYLAC® PA-758
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | POLYLAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GYd782_POLYLAC-PA-758.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYLAC® PA-758 is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.08 | g/cm³ | ASTM D792 |
| 23°C | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 3.0 | g/10 min | |
| 220°C/10.0 kg | 34 | g/10 min | |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 34.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ASTM D785 | |
| Ball Indentation Hardness (H 358/30) | 90.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 42.0 | MPa | ISO 527-2/50 |
| Break | 33.0 | MPa | ISO 527-2/50 |
| 3.00 mm 1 | 39.7 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break, 3.00 mm 2 | 40 | % | ASTM D638 |
| Break | 50 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 6.00 mm 3 | 1860 | MPa | ASTM D790 |
| -- 4 | 1500 | MPa | ISO 178 |
| Flexural Strength | |||
| 6.00 mm 5 | 53.9 | MPa | ASTM D790 |
| -- 6 | 56.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -- | 12 | kJ/m² | ISO 179 |
| -- | 11 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength | 60 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| 23°C, 3.00 mm | 150 | J/m | ASTM D256 |
| 23°C, 6.00 mm | 160 | J/m | ASTM D256 |
| -- | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 88.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 85.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 99.0 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 96.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ASTM D1525 7 |
| -- | 104 | °C | ISO 306/A50 |
| -- | 106 | °C | ISO 306/A120 |
| -- | 98.0 | °C | ISO 306/B50 |
| -- | 101 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 220 to 250 | °C | |
| Front Temperature | 220 to 250 | °C | |
| Processing (Melt) Temp | 230 to 240 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 4.90 to 7.85 | MPa | |
| Holding Pressure | 1.96 to 4.90 | MPa | |
| Back Pressure | 0.490 to 0.981 | MPa |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 6.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® BGK 15 Black | Radici Plastics | Nylon 6 | Radilon® |
| OTECH PVC OE6537 - Profile | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| SQUARE® LIM1500-40A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |
| Sylvin 8980-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ DX06410 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |