INFUSE™ 9500
| Category: | OBC , Olefin Block Copolymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | INFUSE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GXeC7i_INFUSE-9500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INFUSE™ 9500 Olefin Block Copolymer is a olefin copolymer that has excellent flow characteristics and performs well in a wide range of general purpose thermoplastic elastomer applications, such as injection molding and profile extrusion. INFUSE 9500 provides outstanding haptics in over molding applications with polypropylene (PP) and Polyethylene (PE). In addition, its high crystallization temperature and lower density drive lower production costs by reducing cycle time and reducing part weight. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.877 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Compression Molded) | 69 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant (Compression Molded) | 2.28 | MPa | ASTM D638 |
| Tensile Strength (Break, Compression Molded) | 4.98 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 1200 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 9.50 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 1600 | % | ASTM D412 |
| Tear Strength | 35.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 21°C | 22 | % | |
| 70°C 1 | 55 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 122 | °C | Internal Method |
| TMA 2(2.54 cm) | 97 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 5°C/min |
| 2 . | 1N, 5°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SURPASS® IGs153-A | NOVA Chemicals | HDPE Copolymer | SURPASS® |
| LightSpan® LS4-3354 | NuSil Technology | Silicone | LightSpan® |
| Karina PVC COMPOUND E-869-10/189-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ VERTON™ RV0079 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |
| Lupoy® 1300-10 | LG Chem Ltd. | PC | Lupoy® |