NAXALOY® 760
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | MRC Polymers, Inc. |
| Trademark: | NAXALOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GX3dfQ_NAXALOY-760.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Further information and details are available upon request.
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 55.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus | 2210 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 430 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 104 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | < -17.8 | °C | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 - 271 | °C | |
| Middle Temperature | 260 - 277 | °C | |
| Front Temperature | 271 - 282 | °C | |
| Nozzle Temperature | 260 - 282 | °C | |
| Processing (Melt) Temp | 249 - 271 | °C | |
| Mold Temperature | 48.9 - 82.2 | °C | |
| Injection Pressure | 68.9 - 138 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Cushion | 3.30 - 6.35 | mm |
| Injection instructions |
|---|
| Packing: 50 - 75% of injection pressureHold: 40 - 60% of injection pressureAirflow Rate: 0.8 - 1.0 CFM per lb/hour resin processed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULASINT™ F5400 | ICO Polymers EMEA, A Division of A. Schulman | PP Random Copolymer | SCHULASINT™ |
| SITRAROY 2015 / C94150 | SITRAPLAS GmbH | ASA+PC | SITRAROY |
| Starex TX-0520T | SAMSUNG SDI CO., LTD. | MABS | Starex |
| ESTAPROP H 0560 GFC | Cossa Polimeri S.r.l. | PP Homopolymer | ESTAPROP |
| Durethan® C 38 FAM 000000 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |