ULTEM™ 2310EPR resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GX3Aor_ULTEM2310EPRresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 11 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 0.30 - 0.50 | % | Internal method |
| Flow : 3.20mm | 0.40 - 0.60 | % | Internal method |
| Transverse flow : 3.20mm | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.90 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.50 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 160 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 8580 | MPa | ASTM D638 |
| -- | 8980 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 158 | MPa | ASTM D638 |
| Yield | 160 | MPa | ISO 527-2/5 |
| Fracture 4 | 158 | MPa | ASTM D638 |
| Fracture | 160 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 2.1 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2/5 |
| Fracture 6 | 2.1 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 7 | 9140 | MPa | ASTM D790 |
| -- 8 | 9500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 210 | MPa | ISO 178 |
| Yield, 50.0mm span 9 | 228 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10 | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 11 | ISO 179/1eU | ||
| -30°C | 35 | kJ/m² | ISO 179/1eU |
| 23°C | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C | 85 | J/m | ASTM D256 |
| -30°C 12 | 10 | kJ/m² | ISO 180/1A |
| 23°C 13 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 450 | J/m | ASTM D4812 |
| -30°C 14 | 35 | kJ/m² | ISO 180/1U |
| 23°C 15 | 35 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 9.00 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 205 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 6.40mm | 208 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 16 | 207 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 201 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 205 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 17 | 196 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 217 | °C | ASTM D1525 18 |
| -- | 212 | °C | ISO 306/B50 |
| -- | 214 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 150°C | 1.8E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 150°C | 1.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 150°C | 3.0E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : 23 to 150°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.31 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 19 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.400 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 332 - 399 | °C | |
| Middle Temperature | 338 - 399 | °C | |
| Front Temperature | 343 - 399 | °C | |
| Nozzle Temperature | 343 - 399 | °C | |
| Processing (Melt) Temp | 349 - 399 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | Type 1, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 mm |
| 17 . | 80*10*4 mm |
| 18 . | 标准 B (120°C/h), 载荷2 (50N) |
| 19 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8818-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 4213 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| ACLAR® UltRx 4000 film | Honeywell | PCTFE | ACLAR® |
| POLYFLAM® RIPP 2000 HI | A. Schulman Europe | PP Copolymer | POLYFLAM® |
| API II 505 | API II, Inc. | PS (MIPS) | API II |