Integra™ PP 2200 LE
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | PolySource, LLC |
| Trademark: | Integra™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GWzUMA_IntegraPP2200LE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene Impact Copolymer, Fractional Melt Flow, Heat Stabilized |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 75 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 27.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 500 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1340 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.18 mm | 130 | J/m | ASTM D256 |
| 23°C, 3.18 mm | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 87.8 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALENE® P 100 SGF30 ST F V-0 natural | RIA-Polymers GmbH | PP, Unspecified | RIALENE® |
| Taitacell EPS 351FA | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Thermylene® P6-30FG-0684 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| Titalon® 3315TF | Titan Plastics Compounds Co., Ltd. | Nylon 12 | Titalon® |
| Hiprolon® 11 ECN Black H8L | Arkema | Nylon 1012 | Hiprolon® |