Jampilen HP554P
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Jam Polypropylene Company |
| Trademark: | Jampilen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GWhBG5_Jampilen-HP554P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jampilen HP554P is a high Fluidity polypropylene homopolymer for the production of fine denier staple fiber with improved thermo-bonding ability for nonwoven fabrics. The product exhibits excellent antigasfading properties. Jampilen HP552 offers outstanding process stability and spinning behavior on short-spinning lines and some specific long-spinning lines. The thermal-bonding ability is high and allows the production of nonwoven fabrics with higher tear strength or with lower weight per m² for the same strength. The fabrics made with Jampilen HP552R are characterized by softness, textile-like appearance and tear resistance. The typical applications are overstock for diapers, feminine care products, thermo-bonded nonwoven and incontinence pads. Other applications are wipes, filters and fabrics for the clothing and furniture industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 33.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 12 | % | ASTM D638 |
| Flexural Modulus | 1550 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 95.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 154 | °C | ASTM D1525 1 |
| Accelerated Oven Ageing (150°C) | 120 | hr | ASTM D3012 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michithene R6300 | API Polymers, Inc. | HDPE | Michithene |
| DEXFLEX® 756-67-2 | LyondellBasell Industries | TPO (POE) | DEXFLEX® |
| Lion Idemitsu Composites PPS G140C1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| Lupoy® GN5001RFS | LG Chem Ltd. | PC+ABS | Lupoy® |
| Keyflex® BT GN 7142F | LG Chem Ltd. | TPC-ET | Keyflex® BT |