Cleapact TI-300
| Category: | SBC , Styrene Butadiene Block Copolymer |
| Manufacturer: | DIC Corporation |
| Trademark: | Cleapact |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GWPykL_Cleapact-TI-300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Developed with our unique polymerization technology, Cleapact is a type of styrene copolymer resin that excels in the balance of transparency, shock-resistance and molding capacity. Products in this category have a variety of positive characteristics and meet diverse range of user needs. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.30 to 0.70 | % | Internal Method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 75 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, Injection Molded | 51.0 | MPa | |
| Break, Injection Molded | 35.0 | MPa | |
| Tensile Strain (Break, Injection Molded) | 15 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 2500 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 8.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 86.0 | °C | ISO 306 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Injection Molded) | 89.0 | % | JIS K7105 |
| Haze (Injection Molded) | 3.0 | % | JIS K7105 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 | °C | |
| Drying Time | 3.0 | hr |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 | °C | |
| Drying Time | 3.0 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 299 X 58128 | RTP Company | Nylon 66 | RTP |
| Michimid K4210 | API Polymers, Inc. | Nylon 66 | Michimid |
| HiFill® PP 0112 B AM2 | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| Kuraray Poval® PVA 624 | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| Silastic® Q7-4765 | Dow Corning Corporation | Silicone | Silastic® |