Marlex® HMN TR-945
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | Marlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GWIl4N_Marlex-HMN-TR-945.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Marlex® HMN TR-945 is a High Density Polyethylene material. It is available in Latin America or North America for rotational molding. Important attributes of Marlex® HMN TR-945 are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.945 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | ASTM D1693A | ||
| 10% Igepal, Compression Molded, F50 | 25.0 | hr | |
| 100% Igepal, Compression Molded, F50 | 70.0 | hr |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.17 mm, Rotational Molded) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.17 mm, Rotational Molded) | 460 | % | ASTM D638 |
| Flexural Modulus 3 | ASTM D790 | ||
| 2% Secant : 3.17 mm, Rotational Molded | 740 | MPa | |
| Tangent : 3.17 mm, Rotational Molded | 910 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ARM Impact | |||
| -40°C, 3.20 mm | 92.0 | J | |
| -40°C, 6.35 mm | 223 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.17 mm, Rotational Molded | 64.0 | °C | |
| 1.8 MPa, Unannealed, 3.17 mm, Rotational Molded | 44.0 | °C | |
| Brittleness Temperature | -75.0 | °C | ASTM D746A |
| Vicat Softening Temperature | 118 | °C | ASTM D1525 4 |
| Melting Temperature | 130 | °C | |
| Peak Crystallization Temperature (DSC) | 113 | °C | ASTM D3418 |
| Note Message | |
|---|---|
| 1 . | Type IV, 51 mm/min |
| 2 . | Type IV, 51 mm/min |
| 3 . | 13 mm/min |
| 4 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Synthos EPS® 0513S/CZ | Synthos S.A. | PS (EPS) | Synthos EPS® |
| YUPLENE® B351F | SK Global Chemical | PP Impact Copolymer | YUPLENE® |
| Unichem 7905 | Colorite Polymers | PVC, Unspecified | Unichem |
| Zytel® HTN 52G45HSL BK083 | DuPont Performance Polymers | PPA | Zytel® HTN |
| Karina BLACK PVC COMPOUND 751-48/ 1-F-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |