MAJ'ECO DP364M
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJ'ECO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GVl4ts_MAJ-ECO-DP364M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJ'ECO DP364M is a vegetal fibre polypropylene compound intended for injection moulding. MAJ'ECO DP364M has been developed especially for demanding applications in various engineering sectors. APPLICATIONS Product such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 1.4 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3850 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3350 | MPa | ISO 178 |
| Flexural Stress 2 | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 17 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 156 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 115 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 150 - 190 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | at Yield |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMSTER PF300G8 | Polyram Ram-On Industries | PBT | RAMSTER |
| Xuchuan 6002/B-8006N (Mid-sole) | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| VAMPSTAT A 00U 09 V0 26 | Vamp Tech | ABS | VAMPSTAT |
| Hanwha Total PP HTB52 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| KIBILAC® PW-957 | CHI MEI CORPORATION | ASA | KIBILAC® |