QR Resin QR-5020
| Category: | PEI+PC , Polyether Imide + PC |
| Manufacturer: | QTR, Inc. |
| Trademark: | QR Resin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GVZ8vI_QR-Resin-QR-5020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| QR-5020 is available with Release (R) |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 103 | MPa | ASTM D638 |
| Flexural Modulus | 3170 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 206 | °C | |
| 1.8 MPa, Unannealed | 193 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Rear Temperature | 321 to 343 | °C | |
| Middle Temperature | 327 to 354 | °C | |
| Front Temperature | 343 to 371 | °C | |
| Nozzle Temperature | 338 to 360 | °C | |
| Processing (Melt) Temp | 343 to 371 | °C | |
| Mold Temperature | 132 to 160 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ DP 9052-3-1000 | PolyOne Corporation | HDPE | Maxxam™ |
| RTP ESD 1382 TFE 15 | RTP Company | PPS | RTP |
| FARALLOY® PE-211 | O'Neil Color and Compounding | HDPE | FARALLOY® |
| EL-Lene™ H6105JU | SCG Chemicals Co., Ltd. | HDPE | EL-Lene™ |
| Fortron® 1132L4 | Celanese Corporation | PPS | Fortron® |