InnoClear™ OC-5090
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoClear™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GVHgEz_InnoClear-OC-5090.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OC-5090 is a water clear, semi-flexible polyurethane elastomer formulated for hand-batch or vacuum assisted processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. OC-5090 is low viscosity and uses materials that have excellent U.V. resistant qualities. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.07 | g/cm³ | |
| Hardener | 1.07 | g/cm³ | |
| Base Resin | 1.07 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 50 Mix Ratio by Volume: 50 | ||
| Demold Time | 120 to 240 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.20 | Pa·s | |
| 25°C 2 | 0.75 | Pa·s | |
| 25°C 3 | 1.0 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 13 to 19 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 85 to 95 | ASTM D2240 | |
| Tensile Strength | 14.5 | MPa | ASTM D638 |
| Tensile Elongation at Break | 65 | % | ASTM D638 |
| Tear Strength | 39.4 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 24 hours at 77°F + 16 hours at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYREX® PH-888G | CHI MEI CORPORATION | PS (HIPS) | POLYREX® |
| SCHULADUR® A1 GF 30 HF FR 1 | A. Schulman Europe | PBT+PET | SCHULADUR® |
| Cheng Yu E2325 | Cheng Yu Plastic Company Limited | PET | Cheng Yu |
| Hanwha Total PP BI45W | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| POLYfill PPH TS15040 | Polykemi AB | PP Homopolymer | POLYfill |