SABIC® HDPE B5822
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GVH8Ca_SABICHDPEB5822.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE B5822 is a multimodal HDPE that combines high ESCR and stiffness with good impact resistance. It is typically used for blow moulding of consumer packaging up to 5 l, e.g. for packaging the majority of detergents, cleaners, shampoos and cosmetics. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 22 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 1.2 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance | |||
| Molding 1 | 8.00 | hr | ISO 16770 |
| 10% Igepal CO-630, molded, F50 | 150 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1450 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 29.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | 40.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 12 | % | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | > 1000 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1400 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 29.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/A | ||
| -30°C, molded | 7.0 | kJ/m² | ISO 180/A |
| 23°C, molded | 10 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 129 | °C | ISO 306/A |
| Melting Temperature (DSC) | 133 | °C | ISO 11357-3 |
| Enthalpy Change | 205 | J/g | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | FNCT |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APICAL 300AF929 | Kaneka Corporation | Film, PI | APICAL |
| DJSilicone NE-281 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| DiaAlloy TE-35 | Mitsubishi Rayon America Inc. | PPE | DiaAlloy |
| GAPEX® HT RNP38MU07BK | Ferro Corporation | Nylon+PP | GAPEX® HT |
| ESTOPLAST EP 4020WW26 | Ester Industries Ltd. | PBT | ESTOPLAST EP |