| Message |
|---|
| Polifil® GFABS series compounds combine the most desirable properties of both components allowing for enhanced processability and toughness together with the stiffness of glass. These compounds are used in firearms, automotive applications, and household appliances. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 to 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4620 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 65.5 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 2.0 | % | |
| Break, 23°C | 3.0 | % | |
| Flexural Modulus - Tangent (23°C) | 4140 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 102 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 64 | J/m | ASTM D256 |
| Gardner Impact (23°C, 12.7 mm) | 0.678 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 99.0 | °C | |
| 1.8 MPa, Unannealed | 97.8 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 210 to 221 | °C | |
| Front Temperature | 221 to 232 | °C | |
| Nozzle Temperature | 227 to 232 | °C | |
| Processing (Melt) Temp | 218 to 271 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.172 to 0.517 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-9611U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Durethan® BF 4212 000000 | LANXESS Corporation | PBT | Durethan® |
| LightSpan® LS-3140 | NuSil Technology | Silicone | LightSpan® |
| Sylvin 8240-98FU Grey 9570 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9600-53 Red 6186 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |