FERREX® GPP20CS07NA
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ferro Corporation |
| Trademark: | FERREX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GUXiMS_FERREX-GPP20CS07NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FERREX®GPP20CS07NA is a polypropylene material, and its filler is 21% calcium carbonate filler. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. FERREX®The main features of the GPP20CS07NA are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.6 | % | ASTM D955 |
| Transverse flow | 1.8 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 23.4 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 200 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : 23°C | 1510 | MPa | ASTM D790 |
| Tangent : 23°C | 1670 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 37.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1200 | J/m | ASTM D256 |
| Dart Drop Impact (23°C, 3.18 mm) | 27.1 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 79.4 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 48.9 | °C | ASTM D648 |
| Additional Information |
|---|
| The value listed as Unnotched Izod Impact, ASTM D256, was tested in accordance with ASTM D4812.Elongation @ break, 73°F, ASTM D638: >200% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 199 - 204 | °C | |
| Middle Temperature | 204 - 210 | °C | |
| Front Temperature | 210 - 216 | °C | |
| Nozzle Temperature | 216 - 221 | °C | |
| Mold Temperature | 46.1 - 60.0 | °C | |
| Back Pressure | 0.138 - 0.345 | MPa | |
| Screw Speed | 100 - 150 | rpm | |
| Clamp Tonnage | 2.8 - 4.1 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rainmaker Polypropylene ECHPCC20 | Rainmaker Polymers LLC | PP Homopolymer | Rainmaker Polypropylene |
| TEREZ ABS 3003 | TER HELL PLASTIC GMBH | ABS | TEREZ ABS |
| NYCOA Polyamide 1595 HS | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Huafon T26P | Huafon Group Co., Ltd. | Nylon 66 | Huafon |
| ALTECH® PP-B B 4430/500 MR30 | ALBIS PLASTIC GmbH | PP Copolymer | ALTECH® PP-B |