POLYNIL® PR40 LHS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nilit Plastics |
| Trademark: | POLYNIL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GUNIqk_POLYNIL-PR40-LHS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYNIL® PR40 LHS is an unreiforced recycled Polyamide 66 (Nylon 66) from semi dull fibers for injection molding. This 2.6 viscosity Polyamide 66 resin is heast stabilized.. |
| General Information | |
|---|---|
| Recycled Content |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (23°C) | 1.7 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.5 | % | |
| Saturation, 23°C | 8.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2.50 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 81.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, 23°C | 6.0 | % | |
| Break, 23°C | > 40 | % | |
| Flexural Modulus (23°C) | 2100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 23°C | No Break | ||
| 30°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 5.3 | kJ/m² | |
| 23°C | 5.8 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 225 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 77.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 130 | °C | IEC 60216 |
| Vicat Softening Temperature | 240 | °C | ISO 306/B |
| Melting Temperature | 258 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 2 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 15 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 850 | °C | |
| 3.20 mm | 850 | °C | |
| Oxygen Index | 28 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 20000 hr |
| 2 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIRASON™ 102 | Mitsui Chemicals, Inc. | LDPE | MIRASON™ |
| Rotec® ABS 1001 FRVO/1 | ROMIRA GmbH | ABS | Rotec® ABS |
| Trexprene® A88SCI-HF | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| Nypol® PA A3 T40 HL CNZA0040 NR359 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| LNP™ THERMOCOMP™ PF005S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |