Elastamax™ HTE 3050
| Category: | PVC+NBR , Polyvinyl Chloride + NBR |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Elastamax™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GUIhaq_Elastamax-HTE-3050.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Elastamax™ HTE Series thermoplastic elastomers (TPEs) are based upon compounded blends of PVC resins and nitrile rubber. These elastomeric materials provide outstanding resistance to hydrocarbons and oils, offer excellent weatherability, and are an economical alternative to thermoset rubber and other more costly thermoplastic elastomers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(190°C/5.0 kg) | 42 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 52 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Break | 11.9 | MPa | |
| 100% Strain | 2.91 | MPa | |
| 300% Strain | 7.34 | MPa | |
| Tensile Elongation 3(Break) | 470 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 24.7 | kN/m | ASTM D624 |
| Compression Set | ASTM D395A | ||
| 70°C, 22 hr | 49 | % | |
| 100°C, 22 hr | 58 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -55.0 | °C | ASTM D746 |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type IV, 510 mm/min |
| 3 . | Type IV, 510 mm/min |
| 4 . | Die C, 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| McCann PP M10GHPPCC | McCann Plastics Inc. | PP Homopolymer | McCann PP |
| Mirakutoran® TPU E660MNAT | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Teflon® FEP Film | DuPont Fluoropolymers | FEP | Teflon® FEP |
| DuraForm® Flex | 3D Systems | TPE | DuraForm® |
| OxyVinyls® 450F | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |