STERLENE™ RP0100230U
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | R&P (Pte.) Ltd. |
| Trademark: | STERLENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GTtVAb_STERLENE-RP0100230U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| STERLENE™ RP0100230U is a 30% glass fiber reinforced polypropylene that offers good mechanical properties for applications requiring good dimension stability, rigidity and strength. In comparison to general PP, this grade offers optimum warpage, heat and chemical resistance. It can be processed by injection molding and is highly suitable for application such as home appliances, housewares, utility components & furniture. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8670 | MPa | ISO 527-2/50 |
| Tensile Stress (23°C) | 43.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | < 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 2(23°C) | 6820 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 67.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C, Complete Break) | 5.4 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 149 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 118 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 240 | °C | |
| Mold Temperature | 25.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure B |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E395 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Tecomid® NB40 GR20 NL | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| VINIKA® D2151A | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | VINIKA® |
| Karina CREPE PVC COMPOUND TR-605-22/ 23 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Starex VE-1897 | LOTTE ADVANCED MATERIALS CO., LTD. | PS (HIPS) | Starex |