RTP 3499-3 X 102947 B
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GToA70_RTP-3499-3-X-102947-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermally Conductive - Electrically Insulative |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.70 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12400 | MPa | ASTM D638 |
| Tensile Strength | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 0.70 | % | ASTM D638 |
| Flexural Modulus | 12800 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 32 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 130 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 241 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow | 1.7E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 6.9E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity 1 | 1.6 | W/m/K | ASTM E1530 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+12 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 8.0 | hr | |
| Dew Point | -28.9 | °C | |
| Processing (Melt) Temp | 332 - 366 | °C | |
| Mold Temperature | 65.6 - 121 | °C | |
| Injection Pressure | 82.7 - 124 | MPa |
| Injection instructions |
|---|
| The key to successfully molding this material is to start mold open cycles as soon as the screw reaches its retracted position. |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLPLAST TC 1000A | UTEKSOL d.o.o. | SBS | SOLPLAST TC |
| ASI POLYPROPYLENE 1404-01 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| Karina BLACK PVC COMPOUND 722-48/ 1-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OTECH ALLOY OTO9141LSZH - Riser Jacket | OTECH Corporation | TP, Unspecified | OTECH ALLOY |
| LG MABS TR530F | LG Chem Ltd. | MABS | LG MABS |