AKROMID® S3 GF 30 4 black (3429)
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GTfxIL_AKROMID-S3-GF-30-4-black-3429-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® S3 GF 30 4 black (3429) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance. Applications are technical components of cooling water cycles in the automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.31 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 40.0 | -- | cm | Internal Method |
| Humidity Absorption - 62% RH (70°C) | 1.2 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 5.5 | -- | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 195 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8600 | 6200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 160 | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 5.5 | 6.5 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 7700 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 230 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 12 | -- | kJ/m² | |
| 23°C | 16 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 110 | -- | kJ/m² | |
| 23°C | 110 | 90 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 200 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 140 | -- | °C | ISO 75-2/C |
| Melting Temperature 4 | 220 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRILOY® MH275M | Samyang Corporation | PC+ABS | TRILOY® |
| ALCOM® PA66 910/1.1 CF30 PTFE15 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| Geon™ Vinyl Flexible C8065 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Huafon HF-3085A | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Hostacom ERC 161N G21259 | LyondellBasell Industries | PP Copolymer | Hostacom |