Lucalen A2700H

Category:	LDPE , Low Density Polyethylene
Manufacturer:	LyondellBasell Industries
Trademark:	Lucalen
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	GTPUb7_Lucalen-A2700H.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Lucalen A2700H is a low density polyethylene, containing butyl acrylate comonomer.
It exhibits low stiffness, low hardness and good impact properties at low temperature.
Lucalen A2700H is suitable for industrial applications where a combination of good processability and excellent softness is required.
It is compatible with other Lucalen grades and is miscible with other ethylene copolymers, PE-LD, PE-HD and PE-LLD.
The grade is available in natural pellet form.

This grade is not intended for use in medical or pharmaceutical applications.

General Information
Features	Durable Good Adhesion Good Chemical Resistance Good Colorability Good Flexibility Good Processability High ESCR (Stress Crack Resist.) High Impact Resistance Low Hardness Low Temperature Flexibility Low Temperature Impact Resistance Opticals Paintable Soft Weldable
Uses	Cast Film Film Geo Membranes Industrial Applications Plastics Modification Profiles Sheet Wire & Cable Applications
Appearance	Natural Color
Forms	Pellets
Processing Method	Blown Film Cast Film Compression Molding Extrusion Pipe Extrusion Sheet Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.922	g/cm³	ISO 1183/A
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.4	g/10 min	ISO 1133
Environmental Stress-Cracking Resistance	> 1600	hr	ASTM D1693

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D)	34		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Break, Compression Molded)	12.0	MPa	ISO 527-2/5A
Tensile Strain (Break, Compression Molded)	> 800	%	ISO 527-2/5A
Flexural Modulus	50.0	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact Strength (-40°C)	No Break		ISO 180/1A

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	70.0	°C	ISO 306/A50
Melting Temperature	97.0	°C	DSC

Extrusion	Nominal Value	Unit
Melt Temperature	180 to 200	°C

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC X4597	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
Quadrant EPP Nylatron® GSM	Quadrant Engineering Plastic Products	Nylon 6	Quadrant EPP
UNITREX® CM3801	Nytef Plastics, Ltd.	PEEK	UNITREX®
Hostaform® C 2521 G	Celanese Corporation	Acetal (POM) Copolymer	Hostaform®
Shida 030E	JINJIANG City SHIDA Plastic Fine Co., Ltd.	SBS	Shida